- 密度 [g/cm3]: 1.78
- 吸水率 [%]: 0.08
- 缺口冲击强度: 0.55
- 弯曲强度 [MPa]: 55.0
- 弯曲模量 [MPa]: 15.9
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.550 g/cc | 0.0199 lb/in³ | Powder; ASTM D1895 | ||
| Density | 1.78 g/cc | 0.0643 lb/in³ | ASTM D-792 | ||
| Water Absorption | 0.080 % | 0.080 % | 24 hour; ASTM D570 | ||
| 0.25 % | 0.25 % | 48 hour; ASTM D570 | |||
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell E | 80 | 80 | ASTM D785 | ||
| Tensile Strength, Ultimate | 55.0 MPa | 7980 psi | ASTM D638 | ||
| Flexural Strength | 103 MPa | 14900 psi | ASTM D790 | ||
| Flexural Modulus | 15.9 GPa | 2310 ksi | ASTM D790 | ||
| Compressive Strength | 190 MPa | 27600 psi | ASTM D695 | ||
| Izod Impact, Notched | 0.550 J/cm | 1.03 ft-lb/in | ASTM D256A | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 12.2 kV/mm | 310 kV/in | 60 Hz, wet, SS; ASTM D149 | ||
| 14.0 kV/mm | 356 kV/in | ST; ASTM D149 | |||
| Arc Resistance | 185 sec | 185 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 20.0 °C | 11.1 µin/in-°F @Temperature 68.0 °F | ASTM E831 | ||
| CTE, linear, Transverse to Flow | 39.0 µm/m-°C @Temperature 20.0 °C | 21.7 µin/in-°F @Temperature 68.0 °F | ASTM E831 | ||
| Thermal Conductivity | 0.790 W/m-K | 5.48 BTU-in/hr-ft²-°F | ASTM C518 | ||
| Maximum Service Temperature, Air | 150 °C | 302 °F | UL Temperature Index; UL 746B | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | As Molded; ASTM D648A | ||
| >= 282 °C | >= 540 °F | Post Baked; ASTM D648A | |||
| Flammability, UL94 | V-1 @Thickness 3.20 mm | V-1 @Thickness 0.126 in | |||
| Descriptive Properties | |||||
| Available Molding Grades | Compression, Transfer, Injection | ||||
| Color | Black | ||||
| Form | Pellet | ||||