- 密度 [g/cm3]: 1.55
- 吸水率 [%]: 0.2
- 缺口冲击强度: 0.22
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 - 1.62 g/cc | 0.0560 - 0.0585 lb/in³ | Molding; IS 867-1963 |
| Apparent Bulk Density | 0.750 - 0.840 g/cc | 0.0271 - 0.0303 lb/in³ | IS 867-1963 |
| Water Absorption | 0.20 - 0.30 % | 0.20 - 0.30 % | IS 13411-1993 |
| Linear Mold Shrinkage | 0.0035 - 0.0050 cm/cm | 0.0035 - 0.0050 in/in | IS 13411-1992 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 40.0 - 50.0 MPa | 5800 - 7250 psi | 5 mm/min.; IS 867-1963 |
| Shear Strength | 55.0 - 60.0 MPa | 7980 - 8700 psi | IS 867-1963 |
| Izod Impact, Notched | 0.220 - 0.320 J/cm | 0.412 - 0.599 ft-lb/in | IS 13411-1992 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 160 - 170 °C | 320 - 338 °F | |
| Injection Pressure | 15.68 - 34.3 MPa | 2274 - 4970 psi | Mold Pressure |
| Cure Time | 0.417 - 0.667 min | 0.00694 - 0.0111 hour | per mm |
| Shelf Life | 12.0 Month | 12.0 Month | 10-25°C |