- 密度 [g/cm3]: 1.4
- 吸水率 [%]: 0.12
- 缺口冲击强度: 0.25
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 - 1.46 g/cc | 0.0506 - 0.0527 lb/in³ | Molding; IS 867-1963 |
| Apparent Bulk Density | 0.200 - 0.300 g/cc | 0.00723 - 0.0108 lb/in³ | IS 867-1963 |
| Water Absorption | 0.12 - 0.22 % | 0.12 - 0.22 % | IS 13411-1993 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | IS 13411-1992 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 46.0 - 55.0 MPa | 6670 - 7980 psi | 5 mm/min.; IS 867-1963 |
| Shear Strength | 70.0 - 80.0 MPa | 10200 - 11600 psi | 2mm/min.; IS 867-1963 |
| Izod Impact, Notched | 0.250 - 0.300 J/cm | 0.468 - 0.562 ft-lb/in | IS 13411-1992 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 3.16e+11 - 3.16e+12 ohm-cm | 3.16e+11 - 3.16e+12 ohm-cm | IS 3396-1979 |
| Surface Resistance | 1.00e+11 - 1.00e+12 ohm | 1.00e+11 - 1.00e+12 ohm | IS 3396-1979 |
| Dielectric Strength | 7.00 - 9.00 kV/mm @Temperature 90.0 °C | 178 - 229 kV/in @Temperature 194 °F | IS 2584-1963 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 160 - 180 °C | 320 - 356 °F | |
| Injection Pressure | 14.7 - 39.2 MPa | 2130 - 5690 psi | Mold Pressure |
| Cure Time | 1.50 - 1.83 min | 0.0250 - 0.0306 hour | per mm |
| Shelf Life | 12.0 Month | 12.0 Month | 10-25°C |