- 密度 [g/cm3]: 1.37
- 吸水率 [%]: 0.2
- 缺口冲击强度: 0.22
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 - 1.42 g/cc | 0.0495 - 0.0513 lb/in³ | Molding; IS 867-1963 |
| Apparent Bulk Density | 0.640 - 0.700 g/cc | 0.0231 - 0.0253 lb/in³ | IS 867-1963 |
| Water Absorption | 0.20 - 0.60 % | 0.20 - 0.60 % | IS 13411-1993 |
| Linear Mold Shrinkage | 0.0060 - 0.0077 cm/cm | 0.0060 - 0.0077 in/in | IS 13411-1992 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 46.0 - 55.0 MPa | 6670 - 7980 psi | 5 mm/min.; IS 867-1963 |
| Shear Strength | 66.0 - 75.0 MPa | 9570 - 10900 psi | 2mm/min.; IS 867-1963 |
| Izod Impact, Notched | 0.220 - 0.300 J/cm | 0.412 - 0.562 ft-lb/in | IS 13411-1992 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+11 - 3.16e+11 ohm-cm | 1.00e+11 - 3.16e+11 ohm-cm | IS 3396-1979 |
| Surface Resistance | 1.00e+10 - 3.16e+10 ohm | 1.00e+10 - 3.16e+10 ohm | IS 3396-1979 |
| Dielectric Strength | 4.00 - 5.00 kV/mm @Temperature 90.0 °C | 102 - 127 kV/in @Temperature 194 °F | IS 2584-1963 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 160 - 170 °C | 320 - 338 °F | |
| Injection Pressure | 15.68 - 34.3 MPa | 2274 - 4970 psi | Mold Pressure |
| Cure Time | 0.333 - 0.500 min | 0.00556 - 0.00833 hour | per mm |
| Shelf Life | 1.50 Month | 1.50 Month | 27-30°C |
| 4.00 Month | 4.00 Month | below 20°C | |