- 密度 [g/cm3]: 1.6
- 吸水率 [%]: 0.2
- 缺口冲击强度: 0.6
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 - 1.70 g/cc | 0.0578 - 0.0614 lb/in³ | Molding; IS 867-1963 |
| Apparent Bulk Density | 0.650 - 0.720 g/cc | 0.0235 - 0.0260 lb/in³ | IS 867-1963 |
| Water Absorption | 0.20 - 0.35 % | 0.20 - 0.35 % | IS 13411-1993 |
| Linear Mold Shrinkage | 0.0030 - 0.0038 cm/cm | 0.0030 - 0.0038 in/in | IS 13411-1992 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 65.0 - 75.0 MPa | 9430 - 10900 psi | 5 mm/min.; IS 867-1963 |
| Shear Strength | 85.0 - 95.0 MPa | 12300 - 13800 psi | IS 867-1963 |
| Izod Impact, Notched | 0.600 - 0.700 J/cm | 1.12 - 1.31 ft-lb/in | IS 13411-1992 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 3.2e+11 - 1.0e+12 ohm-cm | 3.2e+11 - 1.0e+12 ohm-cm | IS 3396-1979 |
| Surface Resistance | 1.00e+11 - 3.16e+11 ohm | 1.00e+11 - 3.16e+11 ohm | IS 3396-1979 |
| Dielectric Strength | 6.50 - 8.00 kV/mm @Temperature 90.0 °C | 165 - 203 kV/in @Temperature 194 °F | IS 2584-1963 |
| Comparative Tracking Index | >= 175 V | >= 175 V | 2824-1975 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 160 - 180 °C | 320 - 356 °F | |
| Injection Pressure | 15.68 - 34.3 MPa | 2274 - 4970 psi | Mold Pressure |
| Cure Time | 1.33 - 1.67 min | 0.0222 - 0.0278 hour | per mm |
| Shelf Life | 4.00 Month | 4.00 Month | 10-25°C |