- 拉伸强度 [MPa]: 55.2
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.20 - 1.30 g/cc @Thickness 1.57 mm | 1.20 - 1.30 g/cc @Thickness 0.0620 in | ASTM D792 | ||
| Moisture Absorption at Equilibrium | 0.30 % @Thickness 1.57 mm | 0.30 % @Thickness 0.0620 in | ASTM D229 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 80 - 100 @Thickness 1.57 mm | 80 - 100 @Thickness 0.0620 in | ASTM D785 | ||
| Tensile Strength, Yield | 55.2 MPa @Thickness 1.57 mm | 8000 psi @Thickness 0.0620 in | LW; ASTM D638 | ||
| 55.2 MPa @Thickness 1.57 mm | 8000 psi @Thickness 0.0620 in | CW; ASTM D638 | |||
| Modulus of Elasticity | 3.79 GPa @Thickness 1.57 mm | 550 ksi @Thickness 0.0620 in | CW; ASTM D229 | ||
| 4.83 GPa @Thickness 1.57 mm | 700 ksi @Thickness 0.0620 in | LW; ASTM D229 | |||
| Flexural Strength | 75.8 MPa @Thickness 1.57 mm | 11000 psi @Thickness 0.0620 in | CW; ASTM D790 | ||
| 96.5 MPa @Thickness 1.57 mm | 14000 psi @Thickness 0.0620 in | LW; ASTM D790 | |||
| Compressive Strength | 172 MPa @Thickness 12.7 mm | 25000 psi @Thickness 0.500 in | ASTM D695 | ||
| Shear Strength | 96.5 MPa @Thickness 15.7 mm | 14000 psi @Thickness 0.620 in | ASTM D732 | ||
| Izod Impact, Unnotched | 1.44 J/cm @Thickness 12.7 mm | 2.70 ft-lb/in @Thickness 0.500 in | CW, Cond E-48/50; ASTM D256 | ||
| 1.82 J/cm @Thickness 12.7 mm | 3.40 ft-lb/in @Thickness 0.500 in | LW, Cond E-48/50; ASTM D256 | |||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 3.75 @Thickness 1.57 mm | 3.75 @Thickness 0.0620 in | Permittivity, Cond D-24/23; ASTM D150 | ||
| Dielectric Strength | 19.7 kV/mm @Thickness 1.57 mm | 500 kV/in @Thickness 0.0620 in | Cond D-48/50; ASTM D229 S.T. | ||
| 25.6 kV/mm @Thickness 1.57 mm | 650 kV/in @Thickness 0.0620 in | Cond A; ASTM D229 S.T. | |||
| Dielectric Breakdown | 45000 V @Thickness 1.57 mm | 45000 V @Thickness 0.0620 in | Cond D-48/50; ASTM D229 S/S | ||
| 65000 V @Thickness 1.57 mm | 65000 V @Thickness 0.0620 in | Cond A; ASTM D229 S/S | |||
| Dissipation Factor | 0.035 @Thickness 1.57 mm | 0.035 @Thickness 0.0620 in | Cond D-24/23; ASTM D150 | ||
| Arc Resistance | 17 sec @Thickness 3.17 mm | 17 sec @Thickness 0.125 in | ASTM D495 | ||
| Comparative Tracking Index | 150 V @Thickness 3.17 mm | 150 V @Thickness 0.125 in | ASTM D3638 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 95.0 µm/m-°C @Thickness 1.57 mm, Temperature 20.0 °C | 52.8 µin/in-°F @Thickness 0.0620 in, Temperature 68.0 °F | x-axis; IPC-TM 650-2.4.24 | ||
| CTE, linear, Transverse to Flow | 120 µm/m-°C @Thickness 1.57 mm, Temperature 20.0 °C | 66.7 µin/in-°F @Thickness 0.0620 in, Temperature 68.0 °F | x-axis; IPC-TM 650-2.4.24 | ||
| Maximum Service Temperature, Air | 105 °C | 221 °F | |||
| Flammability, UL94 | HB @Thickness 1.57 mm | HB @Thickness 0.0620 in | |||
| Descriptive Properties | |||||
| Bond Strength | 1800 lb | 0.5", ASTM D229 | |||
| Color | Natural | ||||