- 拉伸强度 [MPa]: 110.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.30 - 1.40 g/cc @Thickness 1.57 mm | 1.30 - 1.40 g/cc @Thickness 0.0620 in | ASTM D792 | ||
| Moisture Absorption at Equilibrium | 3.5 % @Thickness 1.57 mm | 3.5 % @Thickness 0.0620 in | ASTM D229 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 90 - 110 @Thickness 1.57 mm | 90 - 110 @Thickness 0.0620 in | ASTM D785 | ||
| Tensile Strength, Yield | 110 MPa @Thickness 1.57 mm | 16000 psi @Thickness 0.0620 in | CW; ASTM D638 | ||
| 138 MPa @Thickness 1.57 mm | 20000 psi @Thickness 0.0620 in | LW; ASTM D638 | |||
| Modulus of Elasticity | 9.65 GPa @Thickness 1.57 mm | 1400 ksi @Thickness 0.0620 in | CW; ASTM D229 | ||
| 13.1 GPa @Thickness 1.57 mm | 1900 ksi @Thickness 0.0620 in | LW; ASTM D229 | |||
| Flexural Strength | 152 MPa @Thickness 1.57 mm | 22000 psi @Thickness 0.0620 in | CW; ASTM D790 | ||
| 200 MPa @Thickness 1.57 mm | 29000 psi @Thickness 0.0620 in | LW; ASTM D790 | |||
| Compressive Strength | 338 MPa @Thickness 12.7 mm | 49000 psi @Thickness 0.500 in | ASTM D695 | ||
| Shear Strength | 96.5 MPa @Thickness 15.7 mm | 14000 psi @Thickness 0.620 in | ASTM D732 | ||
| Izod Impact, Unnotched | 0.374 J/cm @Thickness 12.7 mm | 0.700 ft-lb/in @Thickness 0.500 in | CW, Cond E-48/50; ASTM D256 | ||
| 0.400 J/cm @Thickness 12.7 mm | 0.750 ft-lb/in @Thickness 0.500 in | LW, Cond E-48/50; ASTM D256 | |||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 5.45 @Thickness 1.57 mm | 5.45 @Thickness 0.0620 in | Permittivity, Cond D-24/23; ASTM D150 | ||
| Dielectric Strength | 11.8 kV/mm @Thickness 1.57 mm | 300 kV/in @Thickness 0.0620 in | Cond D-48/50; ASTM D229 S.T. | ||
| 19.7 kV/mm @Thickness 1.57 mm | 500 kV/in @Thickness 0.0620 in | Cond A; ASTM D229 S.T. | |||
| Dielectric Breakdown | 10000 V @Thickness 1.57 mm | 10000 V @Thickness 0.0620 in | Cond D-48/50; ASTM D229 S/S | ||
| 47000 V @Thickness 1.57 mm | 47000 V @Thickness 0.0620 in | Cond A; ASTM D229 S/S | |||
| Dissipation Factor | 0.45 @Thickness 1.57 mm | 0.45 @Thickness 0.0620 in | Cond D-24/23; ASTM D150 | ||
| Arc Resistance | 60 sec @Thickness 3.17 mm | 60 sec @Thickness 0.125 in | ASTM D495 | ||
| Comparative Tracking Index | 150 V @Thickness 3.17 mm | 150 V @Thickness 0.125 in | ASTM D3638 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 17.0 µm/m-°C @Thickness 1.57 mm, Temperature 20.0 °C | 9.44 µin/in-°F @Thickness 0.0620 in, Temperature 68.0 °F | x-axis; IPC-TM 650-2.4.24 | ||
| CTE, linear, Transverse to Flow | 13.0 µm/m-°C @Thickness 1.57 mm, Temperature 20.0 °C | 7.22 µin/in-°F @Thickness 0.0620 in, Temperature 68.0 °F | x-axis; IPC-TM 650-2.4.24 | ||
| Maximum Service Temperature, Air | 130 °C | 266 °F | |||
| Flammability, UL94 | HB @Thickness 1.57 mm | HB @Thickness 0.0620 in | |||
| Descriptive Properties | |||||
| Bond Strength | 1100 lb | 0.5", ASTM D229 | |||
| Color | Natural, Black | ||||