- 密度 [g/cm3]: 1.37
- 吸水率 [%]: 0.63
- 缺口冲击强度: 0.178
- 弯曲强度 [MPa]: 57.0
- 弯曲模量 [MPa]: 6.90
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.600 g/cc | 0.0217 lb/in³ | ASTM D1895 |
| Density | 1.37 g/cc | 0.0495 lb/in³ | ASTM D792 |
| Water Absorption | 0.63 % | 0.63 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 72 | 72 | ASTM D785 |
| Tensile Strength, Ultimate | 57.0 MPa | 8270 psi | ASTM D638 |
| Elongation at Break | 0.98 % | 0.98 % | ASTM D638 |
| Tensile Modulus | 7.30 GPa | 1060 ksi | ASTM D638 |
| Flexural Strength | 88.0 MPa | 12800 psi | ASTM D790 |
| Flexural Modulus | 6.90 GPa | 1000 ksi | ASTM D790 |
| Compressive Strength | 190 MPa | 27600 psi | ASTM D695 |
| Poissons Ratio | 0.35 | 0.35 | ASTM D638 |
| Shear Modulus | 2.70 GPa | 392 ksi | Calculated |
| Izod Impact, Notched | 0.178 J/cm | 0.333 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.192 J/cm² | 0.914 ft-lb/in² | ASTM D256 |
| Impact | 109 | 109 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 5.90e+12 ohm-cm | 5.90e+12 ohm-cm | ASTM D247 |
| Dielectric Constant | 6.2 | 6.2 | ASTM D150 |
| Dielectric Strength | 9.20 kV/mm | 234 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.058 | 0.058 | ASTM D150 |
| Arc Resistance | 134 sec | 134 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 67.0 µm/m-°C @Temperature 40.0 - 130 °C | 37.2 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Maximum Service Temperature, Air | 183 °C | 361 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 351 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |
| Shrinkage | 0.51 % | 0.51 % | 72 hr, 120ºC; ASTM D1299 |