- 密度 [g/cm3]: 1.4
- 吸水率 [%]: 0.36
- 缺口冲击强度: 0.183
- 弯曲强度 [MPa]: 58.0
- 弯曲模量 [MPa]: 6.90
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.600 g/cc | 0.0217 lb/in³ | ASTM D1895 |
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D792 |
| Water Absorption | 0.36 % | 0.36 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0101 cm/cm | 0.0101 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 89 | 89 | ASTM D785 |
| Tensile Strength, Ultimate | 58.0 MPa | 8410 psi | ASTM D638 |
| Elongation at Break | 0.77 % | 0.77 % | ASTM D638 |
| Tensile Modulus | 8.40 GPa | 1220 ksi | ASTM D638 |
| Flexural Strength | 77.0 MPa | 11200 psi | ASTM D790 |
| Flexural Modulus | 6.90 GPa | 1000 ksi | ASTM D790 |
| Compressive Strength | 213 MPa | 30900 psi | ASTM D695 |
| Poissons Ratio | 0.34 | 0.34 | ASTM D638 |
| Shear Modulus | 3.13 GPa | 454 ksi | Calculated |
| Izod Impact, Notched | 0.183 J/cm | 0.343 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.188 J/cm² | 0.895 ft-lb/in² | ASTM D256 |
| Impact | 100 | 100 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.70e+12 ohm-cm | 1.70e+12 ohm-cm | ASTM D247 |
| Dielectric Constant | 4.4 | 4.4 | ASTM D150 |
| Dielectric Strength | 10.1 kV/mm | 257 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.047 | 0.047 | ASTM D150 |
| Arc Resistance | 134 sec | 134 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 54.0 µm/m-°C @Temperature 40.0 - 130 °C | 30.0 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Maximum Service Temperature, Air | 200 °C | 392 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 6.00 mm | V-0 @Thickness 0.236 in | |
| Shrinkage | 0.33 % | 0.33 % | 72 hr, 120ºC; ASTM D1299 |