- 密度 [g/cm3]: 1.37
- 吸水率 [%]: 0.34
- 缺口冲击强度: 0.189
- 弯曲强度 [MPa]: 54.0
- 弯曲模量 [MPa]: 7.50
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.590 g/cc | 0.0213 lb/in³ | ASTM D1895 |
| Density | 1.37 g/cc | 0.0495 lb/in³ | ASTM D792 |
| Water Absorption | 0.34 % | 0.34 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0069 cm/cm | 0.0069 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 88 | 88 | ASTM D785 |
| Tensile Strength, Ultimate | 54.0 MPa | 7830 psi | ASTM D638 |
| Elongation at Break | 0.79 % | 0.79 % | ASTM D638 |
| Tensile Modulus | 7.80 GPa | 1130 ksi | ASTM D638 |
| Flexural Strength | 86.0 MPa | 12500 psi | ASTM D790 |
| Flexural Modulus | 7.50 GPa | 1090 ksi | ASTM D790 |
| Compressive Strength | 212 MPa | 30700 psi | ASTM D695 |
| Izod Impact, Notched | 0.189 J/cm | 0.354 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.195 J/cm² | 0.928 ft-lb/in² | ASTM D256 |
| Impact | 110 | 110 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 3.60e+11 ohm-cm | 3.60e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.0 | 5.0 | ASTM D150 |
| Dielectric Strength | 11.8 kV/mm | 300 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.063 | 0.063 | ASTM D150 |
| Arc Resistance | 125 sec | 125 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 65.0 µm/m-°C @Temperature 40.0 - 130 °C | 36.1 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.340 W/m-K @Temperature 100 °C | 2.36 BTU-in/hr-ft²-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 197 °C | 387 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 162 °C | 324 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |
| Oxygen Index | 25.8 % | 25.8 % | ASTM D2863 |
| Shrinkage | 0.263 % | 0.263 % | 72 hr, 120ºC; ASTM D1299 |