- 密度 [g/cm3]: 1.4
- 吸水率 [%]: 0.47
- 缺口冲击强度: 0.188
- 弯曲强度 [MPa]: 51.0
- 弯曲模量 [MPa]: 8.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.600 g/cc | 0.0217 lb/in³ | ASTM D1895 |
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D792 |
| Water Absorption | 0.47 % | 0.47 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0044 cm/cm | 0.0044 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 87 | 87 | ASTM D785 |
| Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
| Elongation at Break | 0.68 % | 0.68 % | ASTM D638 |
| Tensile Modulus | 8.50 GPa | 1230 ksi | ASTM D638 |
| Flexural Strength | 87.0 MPa | 12600 psi | ASTM D790 |
| Flexural Modulus | 8.00 GPa | 1160 ksi | ASTM D790 |
| Compressive Strength | 207 MPa | 30000 psi | ASTM D695 |
| Izod Impact, Notched | 0.188 J/cm | 0.352 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.188 J/cm² | 0.895 ft-lb/in² | ASTM D256 |
| Impact | 122 | 122 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.20e+12 ohm-cm | 1.20e+12 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.2 | 5.2 | ASTM D150 |
| Dielectric Strength | 14.2 kV/mm | 361 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.051 | 0.051 | ASTM D150 |
| Arc Resistance | 136 sec | 136 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 63.0 µm/m-°C @Temperature 40.0 - 130 °C | 35.0 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.400 W/m-K @Temperature 100 °C | 2.78 BTU-in/hr-ft²-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 193 °C | 379 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 6.00 mm | V-0 @Thickness 0.236 in | |
| Oxygen Index | 27.6 % | 27.6 % | ASTM D2863 |
| Shrinkage | 0.208 % | 0.208 % | 72 hr, 120ºC; ASTM D1299 |