- 密度 [g/cm3]: 1.37
- 吸水率 [%]: 0.63
- 缺口冲击强度: 0.166
- 弯曲强度 [MPa]: 62.0
- 弯曲模量 [MPa]: 6.60
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.600 g/cc | 0.0217 lb/in³ | ASTM D1895 |
| Density | 1.37 g/cc | 0.0495 lb/in³ | ASTM D792 |
| Water Absorption | 0.63 % | 0.63 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0084 cm/cm | 0.0084 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 71 | 71 | ASTM D785 |
| Tensile Strength, Ultimate | 62.0 MPa | 8990 psi | ASTM D638 |
| Elongation at Break | 1.02 % | 1.02 % | ASTM D638 |
| Tensile Modulus | 7.40 GPa | 1070 ksi | ASTM D638 |
| Flexural Strength | 88.0 MPa | 12800 psi | ASTM D790 |
| Flexural Modulus | 6.60 GPa | 957 ksi | ASTM D790 |
| Compressive Strength | 182 MPa | 26400 psi | ASTM D695 |
| Poissons Ratio | 0.36 | 0.36 | ASTM D638 |
| Shear Modulus | 2.72 GPa | 395 ksi | Calculated |
| Izod Impact, Notched | 0.166 J/cm | 0.311 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.182 J/cm² | 0.866 ft-lb/in² | ASTM D256 |
| Impact | 111 | 111 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.20e+13 ohm-cm | 1.20e+13 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.7 | 5.7 | ASTM D150 |
| Dielectric Strength | 9.90 kV/mm | 251 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.056 | 0.056 | ASTM D150 |
| Arc Resistance | 135 sec | 135 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 57.0 µm/m-°C @Temperature 40.0 - 130 °C | 31.7 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Maximum Service Temperature, Air | 186 °C | 367 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |
| Shrinkage | 0.58 % | 0.58 % | 72 hr, 120ºC; ASTM D1299 |