- 密度 [g/cm3]: 1.41
- 吸水率 [%]: 0.31
- 断裂伸长率 [%]: 81.1
- 弯曲强度 [MPa]: 57.9
- 弯曲模量 [MPa]: 7.53
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.640 g/cc | 0.0231 lb/in³ | Apparent density per ASTM D1895 |
| Water Absorption | 0.31 % | 0.31 % | ASTM D570 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | per ATM D955. Post shrinkage is 0.29% at 72hr 120ºC per ASTM D1299. |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 86 | 86 | ASTM D785 |
| Tensile Strength, Ultimate | 57.9 MPa | 8400 psi | ASTM D638 |
| Elongation at Break | 0.77 % | 0.77 % | ASTM D638 |
| Tensile Modulus | 8.45 GPa | 1230 ksi | ASTM D638 |
| Flexural Yield Strength | 81.1 MPa | 11800 psi | ASTM D790 |
| Flexural Modulus | 7.53 GPa | 1090 ksi | ASTM D790 |
| Compressive Yield Strength | 199.7 MPa | 28960 psi | ASTM D695 |
| Charpy Impact, Notched | 0.190 J/cm² | 0.904 ft-lb/in² | ASTM D256 |
| Impact | 102 | 102 | J/m Plenco drop ball test |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 5.33e+11 ohm-cm | 5.33e+11 ohm-cm | ASTM D257 |
| Dielectric Constant | 5.3 @Frequency 1e+6 Hz | 5.3 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 9.00 kV/mm | 229 kV/in | Step by Step; ASTM D149 |
| 10.4 kV/mm | 264 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.060 @Frequency 1e+6 Hz | 0.060 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 160 sec | 160 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 200 °C | 392 °F | Heat resistance per ASTM D794 |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | ASTM D648 |
| Flammability, UL94 | V-1 @Thickness 6.10 mm | V-1 @Thickness 0.240 in | |