- 密度 [g/cm3]: 1.55
- 吸水率 [%]: 0.163
- 缺口冲击强度: 0.202
- 弯曲强度 [MPa]: 55.0
- 弯曲模量 [MPa]: 9.40
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.650 g/cc | 0.0235 lb/in³ | ASTM D1895 |
| Density | 1.55 g/cc | 0.0560 lb/in³ | ASTM D792 |
| Water Absorption | 0.163 % | 0.163 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0042 cm/cm | 0.0042 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 79 | 79 | ASTM D785 |
| Tensile Strength, Ultimate | 55.0 MPa | 7980 psi | ASTM D638 |
| Elongation at Break | 0.66 % | 0.66 % | ASTM D638 |
| Tensile Modulus | 10.0 GPa | 1450 ksi | ASTM D638 |
| Flexural Strength | 92.0 MPa | 13300 psi | ASTM D790 |
| Flexural Modulus | 9.40 GPa | 1360 ksi | ASTM D790 |
| Compressive Strength | 172 MPa | 24900 psi | ASTM D695 |
| Poissons Ratio | 0.33 | 0.33 | ASTM D638 |
| Shear Modulus | 3.76 GPa | 545 ksi | Calculated |
| Izod Impact, Notched | 0.202 J/cm | 0.378 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.215 J/cm² | 1.02 ft-lb/in² | ASTM D256 |
| Impact | 92 | 92 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 4.00e+11 ohm-cm | 4.00e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.7 | 5.7 | ASTM D150 |
| Dielectric Strength | 12.0 kV/mm | 305 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.058 | 0.058 | ASTM D150 |
| Arc Resistance | 182 sec | 182 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 46.0 µm/m-°C @Temperature 40.0 - 130 °C | 25.6 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Maximum Service Temperature, Air | 203 °C | 397 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 194 °C | 381 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |
| Oxygen Index | 33 % | 33 % | ASTM D2863 |
| Shrinkage | 0.158 % | 0.158 % | 72 hr, 120ºC; ASTM D1299 |