- 密度 [g/cm3]: 1.59
- 吸水率 [%]: 0.169
- 缺口冲击强度: 0.199
- 弯曲强度 [MPa]: 55.0
- 弯曲模量 [MPa]: 9.30
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.660 g/cc | 0.0238 lb/in³ | ASTM D1895 |
| Density | 1.59 g/cc | 0.0574 lb/in³ | ASTM D792 |
| Water Absorption | 0.169 % | 0.169 % | ASTM D570 |
| Linear Mold Shrinkage | 0.00281 cm/cm | 0.00281 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 84 | 84 | ASTM D785 |
| Tensile Strength, Ultimate | 55.0 MPa | 7980 psi | ASTM D638 |
| Elongation at Break | 0.60 % | 0.60 % | ASTM D638 |
| Tensile Modulus | 11.0 GPa | 1600 ksi | ASTM D638 |
| Flexural Strength | 83.0 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 9.30 GPa | 1350 ksi | ASTM D790 |
| Compressive Strength | 194 MPa | 28100 psi | ASTM D695 |
| Izod Impact, Notched | 0.199 J/cm | 0.373 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.220 J/cm² | 1.05 ft-lb/in² | ASTM D256 |
| Impact | 117 | 117 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 3.30e+12 ohm-cm | 3.30e+12 ohm-cm | ASTM D247 |
| Dielectric Constant | 4.8 | 4.8 | ASTM D150 |
| Dielectric Strength | 14.4 kV/mm | 366 kV/in | Step by Step; ASTM D149 |
| 17.4 kV/mm | 442 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.0274 | 0.0274 | ASTM D150 |
| Arc Resistance | 172 sec | 172 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 58.0 µm/m-°C @Temperature 40.0 - 130 °C | 32.2 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.470 W/m-K @Temperature 100 °C | 3.26 BTU-in/hr-ft²-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 204 °C | 399 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 194 °C | 381 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | |
| Oxygen Index | 38 % | 38 % | ASTM D2863 |
| Shrinkage | 0.086 % | 0.086 % | 72 hr, 120ºC; ASTM D1299 |