- 密度 [g/cm3]: 1.59
- 吸水率 [%]: 0.088
- 缺口冲击强度: 0.16
- 弯曲强度 [MPa]: 44.0
- 弯曲模量 [MPa]: 9.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.680 g/cc | 0.0246 lb/in³ | ASTM D1895 |
| Density | 1.59 g/cc | 0.0574 lb/in³ | ASTM D792 |
| Water Absorption | 0.088 % | 0.088 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0067 cm/cm | 0.0067 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 79 | 79 | ASTM D785 |
| Tensile Strength, Ultimate | 44.0 MPa | 6380 psi | ASTM D638 |
| Elongation at Break | 0.49 % | 0.49 % | ASTM D638 |
| Tensile Modulus | 10.5 GPa | 1520 ksi | ASTM D638 |
| Flexural Strength | 72.0 MPa | 10400 psi | ASTM D790 |
| Flexural Modulus | 9.10 GPa | 1320 ksi | ASTM D790 |
| Compressive Strength | 185 MPa | 26800 psi | ASTM D695 |
| Poissons Ratio | 0.32 | 0.32 | ASTM D638 |
| Shear Modulus | 3.98 GPa | 577 ksi | Calculated |
| Izod Impact, Notched | 0.160 J/cm | 0.300 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.150 J/cm² | 0.714 ft-lb/in² | ASTM D256 |
| Impact | 64 | 64 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 9.30e+11 ohm-cm | 9.30e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.6 | 5.6 | ASTM D150 |
| Dielectric Strength | 9.70 kV/mm | 246 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.045 | 0.045 | ASTM D150 |
| Arc Resistance | 180 sec | 180 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 49.0 µm/m-°C @Temperature 40.0 - 130 °C | 27.2 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.510 W/m-K @Temperature 100 °C | 3.54 BTU-in/hr-ft²-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 220 °C | 428 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 164 °C | 327 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |
| Oxygen Index | 45 % | 45 % | ASTM D2863 |
| Shrinkage | 0.133 % | 0.133 % | 72 hr, 120ºC; ASTM D1299 |