- 密度 [g/cm3]: 1.5
- 吸水率 [%]: 0.24
- 缺口冲击强度: 0.153
- 弯曲强度 [MPa]: 56.0
- 弯曲模量 [MPa]: 8.80
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.660 g/cc | 0.0238 lb/in³ | ASTM D1895 |
| Density | 1.50 g/cc | 0.0542 lb/in³ | ASTM D792 |
| Water Absorption | 0.24 % | 0.24 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0044 cm/cm | 0.0044 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 85 | 85 | ASTM D785 |
| Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ASTM D638 |
| Elongation at Break | 0.63 % | 0.63 % | ASTM D638 |
| Tensile Modulus | 10.1 GPa | 1460 ksi | ASTM D638 |
| Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
| Flexural Modulus | 8.80 GPa | 1280 ksi | ASTM D790 |
| Compressive Strength | 203 MPa | 29400 psi | ASTM D695 |
| Izod Impact, Notched | 0.153 J/cm | 0.287 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.206 J/cm² | 0.980 ft-lb/in² | ASTM D256 |
| Impact | 93 | 93 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.90e+11 ohm-cm | 2.90e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.6 | 5.6 | ASTM D150 |
| Dielectric Strength | 13.2 kV/mm | 335 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.050 | 0.050 | ASTM D150 |
| Arc Resistance | 148 sec | 148 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 0.480 W/m-K @Temperature 100 °C | 3.33 BTU-in/hr-ft²-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 208 °C | 406 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C | 388 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |
| Oxygen Index | 32 % | 32 % | ASTM D2863 |
| Shrinkage | 0.173 % | 0.173 % | 72 hr, 120ºC; ASTM D1299 |