- 密度 [g/cm3]: 1.55
- 吸水率 [%]: 0.135
- 缺口冲击强度: 0.172
- 弯曲强度 [MPa]: 53.0
- 弯曲模量 [MPa]: 9.50
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.610 g/cc | 0.0220 lb/in³ | ASTM D1895 |
| Density | 1.55 g/cc | 0.0560 lb/in³ | ASTM D792 |
| Water Absorption | 0.135 % | 0.135 % | ASTM D570 |
| Linear Mold Shrinkage | 0.00297 cm/cm | 0.00297 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 91 | 91 | ASTM D785 |
| Tensile Strength, Ultimate | 53.0 MPa | 7690 psi | ASTM D638 |
| Elongation at Break | 0.62 % | 0.62 % | ASTM D638 |
| Tensile Modulus | 10.1 GPa | 1460 ksi | ASTM D638 |
| Flexural Strength | 80.0 MPa | 11600 psi | ASTM D790 |
| Flexural Modulus | 9.50 GPa | 1380 ksi | ASTM D790 |
| Compressive Strength | 190 MPa | 27600 psi | ASTM D695 |
| Izod Impact, Notched | 0.172 J/cm | 0.322 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.211 J/cm² | 1.00 ft-lb/in² | ASTM D256 |
| Impact | 104 | 104 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 3.90e+12 ohm-cm | 3.90e+12 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.9 | 5.9 | ASTM D150 |
| Dielectric Strength | 11.2 kV/mm | 284 kV/in | Short Time; ASTM D149 |
| 13.2 kV/mm | 335 kV/in | Step by Step; ASTM D149 | |
| Dissipation Factor | 0.044 | 0.044 | ASTM D150 |
| Arc Resistance | 171 sec | 171 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 51.0 µm/m-°C @Temperature 40.0 - 130 °C | 28.3 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Maximum Service Temperature, Air | 216 °C | 421 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 209 °C | 408 °F | ASTM D648 |
| Oxygen Index | 42 % | 42 % | ASTM D2863 |
| Shrinkage | 0.143 % | 0.143 % | 72 hr, 120ºC; ASTM D1299 |