- 密度 [g/cm3]: 1.83
- 吸水率 [%]: 0.035
- 缺口冲击强度: 0.167
- 弯曲强度 [MPa]: 31.0
- 弯曲模量 [MPa]: 10.6
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.900 g/cc | 0.0325 lb/in³ | ASTM D1895 |
| Density | 1.83 g/cc | 0.0661 lb/in³ | ASTM D792 |
| Water Absorption | 0.035 % | 0.035 % | ASTM D570 |
| Linear Mold Shrinkage | 0.00183 cm/cm | 0.00183 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 59 | 59 | ASTM D785 |
| Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | ASTM D638 |
| Elongation at Break | 0.34 % | 0.34 % | ASTM D638 |
| Tensile Modulus | 10.3 GPa | 1490 ksi | ASTM D638 |
| Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
| Flexural Modulus | 10.6 GPa | 1540 ksi | ASTM D790 |
| Compressive Strength | 130 MPa | 18900 psi | ASTM D695 |
| Izod Impact, Notched | 0.167 J/cm | 0.313 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.179 J/cm² | 0.852 ft-lb/in² | ASTM D256 |
| Impact | 56 | 56 | J/m drop Ball Impact; PLENCO |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 38.0 µm/m-°C @Temperature 40.0 - 130 °C | 21.1 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Maximum Service Temperature, Air | 206 °C | 403 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | ASTM D648 |
| Shrinkage | 0.040 % | 0.040 % | 72 hr, 120ºC; ASTM D1299 |