- 密度 [g/cm3]: 1.74
- 吸水率 [%]: 0.048
- 缺口冲击强度: 0.161
- 弯曲强度 [MPa]: 44.0
- 弯曲模量 [MPa]: 12.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.930 g/cc | 0.0336 lb/in³ | ASTM D1895 |
| Density | 1.74 g/cc | 0.0629 lb/in³ | ASTM D792 |
| Water Absorption | 0.048 % | 0.048 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0042 cm/cm | 0.0042 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 110 | 110 | ASTM D785 |
| Tensile Strength, Ultimate | 44.0 MPa | 6380 psi | ASTM D638 |
| Elongation at Break | 0.32 % | 0.32 % | ASTM D638 |
| Tensile Modulus | 15.3 GPa | 2220 ksi | ASTM D638 |
| Flexural Strength | 73.0 MPa | 10600 psi | ASTM D790 |
| Flexural Modulus | 12.8 GPa | 1860 ksi | ASTM D790 |
| Compressive Strength | 146 MPa | 21200 psi | ASTM D695 |
| Izod Impact, Notched | 0.161 J/cm | 0.302 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.144 J/cm² | 0.685 ft-lb/in² | ASTM D256 |
| Impact | 37 | 37 | J/m drop Ball Impact; PLENCO |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 257 °C | 495 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 181 °C | 358 °F | ASTM D648 |
| Shrinkage | 0.086 % | 0.086 % | 72 hr, 120ºC; ASTM D1299 |