- 密度 [g/cm3]: 1.58
- 吸水率 [%]: 0.4
- 缺口冲击强度: 0.19
- 弯曲强度 [MPa]: 53.0
- 弯曲模量 [MPa]: 8.60
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.620 g/cc | 0.0224 lb/in³ | ASTM D1895 |
| Density | 1.58 g/cc | 0.0571 lb/in³ | ASTM D792 |
| Water Absorption | 0.40 % | 0.40 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0053 cm/cm | 0.0053 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 57 | 57 | ASTM D785 |
| Tensile Strength, Ultimate | 53.0 MPa | 7690 psi | ASTM D638 |
| Elongation at Break | 0.85 % | 0.85 % | ASTM D638 |
| Tensile Modulus | 10.1 GPa | 1460 ksi | ASTM D638 |
| Flexural Strength | 79.0 MPa | 11500 psi | ASTM D790 |
| Flexural Modulus | 8.60 GPa | 1250 ksi | ASTM D790 |
| Compressive Strength | 139 MPa | 20200 psi | ASTM D695 |
| Poissons Ratio | 0.34 | 0.34 | ASTM D638 |
| Shear Modulus | 3.77 GPa | 547 ksi | Calculated |
| Izod Impact, Notched | 0.190 J/cm | 0.356 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.205 J/cm² | 0.976 ft-lb/in² | ASTM D256 |
| Impact | 144 | 144 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.70e+12 ohm-cm | 1.70e+12 ohm-cm | ASTM D247 |
| Dielectric Constant | 6.5 | 6.5 | ASTM D150 |
| Dielectric Strength | 7.30 kV/mm | 185 kV/in | Step by Step; ASTM D149 |
| 9.40 kV/mm | 239 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.162 | 0.162 | ASTM D150 |
| Arc Resistance | 181 sec | 181 sec | ASTM D495 |
| Comparative Tracking Index | 200 V | 200 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 34.0 µm/m-°C @Temperature 40.0 - 130 °C | 18.9 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.550 W/m-K @Temperature 100 °C | 3.82 BTU-in/hr-ft²-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 202 °C | 396 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | ASTM D648 |
| Flammability, UL94 | V-1 @Thickness 1.50 mm | V-1 @Thickness 0.0591 in | |
| Oxygen Index | 31 % | 31 % | ASTM D2863 |
| Shrinkage | 0.34 % | 0.34 % | 72 hr, 120ºC; ASTM D1299 |