- 密度 [g/cm3]: 1.73
- 吸水率 [%]: 0.045
- 缺口冲击强度: 0.166
- 弯曲强度 [MPa]: 40.0
- 弯曲模量 [MPa]: 12.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.850 g/cc | 0.0307 lb/in³ | ASTM D1895 |
| Density | 1.73 g/cc | 0.0625 lb/in³ | ASTM D792 |
| Water Absorption | 0.045 % | 0.045 % | ASTM D570 |
| Linear Mold Shrinkage | 0.00285 cm/cm | 0.00285 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 71 | 71 | ASTM D785 |
| Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | ASTM D638 |
| Elongation at Break | 0.31 % | 0.31 % | ASTM D638 |
| Tensile Modulus | 15.6 GPa | 2260 ksi | ASTM D638 |
| Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
| Flexural Modulus | 12.1 GPa | 1750 ksi | ASTM D790 |
| Compressive Strength | 169 MPa | 24500 psi | ASTM D695 |
| Izod Impact, Notched | 0.166 J/cm | 0.311 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.183 J/cm² | 0.871 ft-lb/in² | ASTM D256 |
| Impact | 69 | 69 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.50e+13 ohm-cm | 1.50e+13 ohm-cm | ASTM D247 |
| Dielectric Constant | 4.6 | 4.6 | ASTM D150 |
| Dielectric Strength | 17.7 kV/mm | 450 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.0172 | 0.0172 | ASTM D150 |
| Arc Resistance | 188 sec | 188 sec | ASTM D495 |
| Comparative Tracking Index | 200 V | 200 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 0.550 W/m-K @Temperature 100 °C | 3.82 BTU-in/hr-ft²-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 225 °C | 437 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |
| Oxygen Index | 43 % | 43 % | ASTM D2863 |
| Shrinkage | 0.040 % | 0.040 % | 72 hr, 120ºC; ASTM D1299 |