- 密度 [g/cm3]: 1.37
- 吸水率 [%]: 0.43
- 缺口冲击强度: 0.208
- 弯曲强度 [MPa]: 49.0
- 弯曲模量 [MPa]: 6.20
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.550 g/cc | 0.0199 lb/in³ | ASTM D1895 |
| Density | 1.37 g/cc | 0.0495 lb/in³ | ASTM D792 |
| Water Absorption | 0.43 % | 0.43 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0106 cm/cm | 0.0106 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 79 | 79 | ASTM D785 |
| Tensile Strength, Ultimate | 49.0 MPa | 7110 psi | ASTM D638 |
| Elongation at Break | 0.67 % | 0.67 % | ASTM D638 |
| Tensile Modulus | 7.80 GPa | 1130 ksi | ASTM D638 |
| Flexural Strength | 69.0 MPa | 10000 psi | ASTM D790 |
| Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D790 |
| Compressive Strength | 188 MPa | 27300 psi | ASTM D695 |
| Poissons Ratio | 0.36 | 0.36 | ASTM D638 |
| Shear Modulus | 2.87 GPa | 416 ksi | Calculated |
| Izod Impact, Notched | 0.208 J/cm | 0.390 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.194 J/cm² | 0.923 ft-lb/in² | ASTM D256 |
| Impact | 148 | 148 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.40e+11 ohm-cm | 1.40e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.4 | 5.4 | ASTM D150 |
| Dielectric Strength | 7.10 kV/mm | 180 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.067 | 0.067 | ASTM D150 |
| Arc Resistance | 119 sec | 119 sec | ASTM D495 |
| Comparative Tracking Index | 150 V | 150 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 53.0 µm/m-°C @Temperature 40.0 - 130 °C | 29.4 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.350 W/m-K @Temperature 100 °C | 2.43 BTU-in/hr-ft²-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 187 °C | 369 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C | 298 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 6.00 mm | V-0 @Thickness 0.236 in | |
| Oxygen Index | 27.2 % | 27.2 % | ASTM D2863 |
| Shrinkage | 0.47 % | 0.47 % | 72 hr, 120ºC; ASTM D1299 |