- 密度 [g/cm3]: 1.5
- 吸水率 [%]: 0.231
- 缺口冲击强度: 0.165
- 弯曲强度 [MPa]: 57.0
- 弯曲模量 [MPa]: 8.30
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.650 g/cc | 0.0235 lb/in³ | ASTM D1895 |
| Density | 1.50 g/cc | 0.0542 lb/in³ | ASTM D792 |
| Water Absorption | 0.231 % | 0.231 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0078 cm/cm | 0.0078 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 99 | 99 | ASTM D785 |
| Tensile Strength, Ultimate | 57.0 MPa | 8270 psi | ASTM D638 |
| Elongation at Break | 0.77 % | 0.77 % | ASTM D638 |
| Tensile Modulus | 9.50 GPa | 1380 ksi | ASTM D638 |
| Flexural Strength | 88.0 MPa | 12800 psi | ASTM D790 |
| Flexural Modulus | 8.30 GPa | 1200 ksi | ASTM D790 |
| Compressive Strength | 180 MPa | 26100 psi | ASTM D695 |
| Poissons Ratio | 0.35 | 0.35 | ASTM D638 |
| Shear Modulus | 3.52 GPa | 511 ksi | Calculated |
| Izod Impact, Notched | 0.165 J/cm | 0.309 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.186 J/cm² | 0.885 ft-lb/in² | ASTM D256 |
| Impact | 100 | 100 | J/m drop Ball Impact; PLENCO |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 50.0 µm/m-°C @Temperature 40.0 - 130 °C | 27.8 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.540 W/m-K @Temperature 100 °C | 3.75 BTU-in/hr-ft²-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 201 °C | 394 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 168 °C | 334 °F | ASTM D648 |
| Oxygen Index | 32 % | 32 % | ASTM D2863 |
| Shrinkage | 0.28 % | 0.28 % | 72 hr, 120ºC; ASTM D1299 |