- 密度 [g/cm3]: 1.86
- 吸水率 [%]: 0.082
- 缺口冲击强度: 0.163
- 弯曲强度 [MPa]: 31.0
- 弯曲模量 [MPa]: 11.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.980 g/cc | 0.0354 lb/in³ | ASTM D1895 |
| Density | 1.86 g/cc | 0.0672 lb/in³ | ASTM D792 |
| Water Absorption | 0.082 % | 0.082 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0031 cm/cm | 0.0031 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 80 | 80 | ASTM D785 |
| Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | ASTM D638 |
| Elongation at Break | 0.272 % | 0.272 % | ASTM D638 |
| Tensile Modulus | 13.4 GPa | 1940 ksi | ASTM D638 |
| Flexural Strength | 60.0 MPa | 8700 psi | ASTM D790 |
| Flexural Modulus | 11.5 GPa | 1670 ksi | ASTM D790 |
| Compressive Strength | 162 MPa | 23500 psi | ASTM D695 |
| Izod Impact, Notched | 0.163 J/cm | 0.305 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.195 J/cm² | 0.928 ft-lb/in² | ASTM D256 |
| Impact | 69 | 69 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.90e+13 ohm-cm | 1.90e+13 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.1 | 5.1 | ASTM D150 |
| Dielectric Strength | 12.2 kV/mm | 310 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.0159 | 0.0159 | ASTM D150 |
| Arc Resistance | 48 sec | 48 sec | ASTM D495 |
| Comparative Tracking Index | 200 V | 200 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 75.0 µm/m-°C @Temperature 40.0 - 130 °C | 41.7 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Maximum Service Temperature, Air | 214 °C | 417 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 188 °C | 370 °F | ASTM D648 |
| Shrinkage | 0.156 % | 0.156 % | 72 hr, 120ºC; ASTM D1299 |