- 密度 [g/cm3]: 1.78
- 吸水率 [%]: 0.057
- 缺口冲击强度: 0.37
- 弯曲强度 [MPa]: 56.0
- 弯曲模量 [MPa]: 16.3
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.770 g/cc | 0.0278 lb/in³ | ASTM D1895 |
| Density | 1.78 g/cc | 0.0643 lb/in³ | ASTM D792 |
| Water Absorption | 0.057 % | 0.057 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0022 cm/cm | 0.0022 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 87 | 87 | ASTM D785 |
| Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ASTM D638 |
| Elongation at Break | 0.37 % | 0.37 % | ASTM D638 |
| Tensile Modulus | 17.1 GPa | 2480 ksi | ASTM D638 |
| Flexural Strength | 123 MPa | 17800 psi | ASTM D790 |
| Flexural Modulus | 16.3 GPa | 2360 ksi | ASTM D790 |
| Compressive Strength | 195 MPa | 28300 psi | ASTM D695 |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.370 J/cm² | 1.76 ft-lb/in² | ASTM D256 |
| Impact | 164 | 164 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.20e+12 ohm-cm | 1.20e+12 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.6 | 5.6 | ASTM D150 |
| Dielectric Strength | 11.6 kV/mm | 295 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.048 | 0.048 | ASTM D150 |
| Arc Resistance | 185 sec | 185 sec | ASTM D495 |
| Comparative Tracking Index | 250 V | 250 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 0.580 W/m-K @Temperature 100 °C | 4.03 BTU-in/hr-ft²-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 241 °C | 466 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C | 532 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.500 mm | V-0 @Thickness 0.0197 in | |
| Oxygen Index | 53 % | 53 % | ASTM D2863 |
| Shrinkage | 0.0282 % | 0.0282 % | 72 hr, 120ºC; ASTM D1299 |