- 密度 [g/cm3]: 1.52
- 吸水率 [%]: 0.44
- 缺口冲击强度: 0.179
- 弯曲强度 [MPa]: 53.0
- 弯曲模量 [MPa]: 7.20
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.620 g/cc | 0.0224 lb/in³ | ASTM D1895 |
| Density | 1.52 g/cc | 0.0549 lb/in³ | ASTM D792 |
| Water Absorption | 0.44 % | 0.44 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0063 cm/cm | 0.0063 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 57 | 57 | ASTM D785 |
| Tensile Strength, Ultimate | 53.0 MPa | 7690 psi | ASTM D638 |
| Elongation at Break | 1.12 % | 1.12 % | ASTM D638 |
| Tensile Modulus | 7.90 GPa | 1150 ksi | ASTM D638 |
| Flexural Strength | 76.0 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 7.20 GPa | 1040 ksi | ASTM D790 |
| Compressive Strength | 157 MPa | 22800 psi | ASTM D695 |
| Poissons Ratio | 0.33 | 0.33 | ASTM D638 |
| Shear Modulus | 2.97 GPa | 431 ksi | Calculated |
| Izod Impact, Notched | 0.179 J/cm | 0.335 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.196 J/cm² | 0.933 ft-lb/in² | ASTM D256 |
| Impact | 125 | 125 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 8.30e+11 ohm-cm | 8.30e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 7.0 | 7.0 | ASTM D150 |
| Dielectric Strength | 8.00 kV/mm | 203 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.172 | 0.172 | ASTM D150 |
| Arc Resistance | 177 sec | 177 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 37.0 µm/m-°C @Temperature 40.0 - 130 °C | 20.6 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.460 W/m-K @Temperature 100 °C | 3.19 BTU-in/hr-ft²-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 204 °C | 399 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 186 °C | 367 °F | ASTM D648 |
| Flammability, UL94 | V-1 @Thickness 1.50 mm | V-1 @Thickness 0.0591 in | |
| Oxygen Index | 31 % | 31 % | ASTM D2863 |
| Shrinkage | 0.42 % | 0.42 % | 72 hr, 120ºC; ASTM D1299 |