- 密度 [g/cm3]: 1.42
- 吸水率 [%]: 0.4
- 断裂伸长率 [%]: 76.0
- 弯曲强度 [MPa]: 55.0
- 弯曲模量 [MPa]: 8.30
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.560 g/cc | 0.0202 lb/in³ | ASTM D1895 |
| Water Absorption | 0.40 % | 0.40 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | Compression; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 55.0 MPa | 7980 psi | ASTM D638 |
| Flexural Yield Strength | 76.0 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 8.30 GPa | 1200 ksi | ASTM D790 |
| Compressive Yield Strength | 221 MPa | 32100 psi | ASTM D695 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.8 @Frequency 1e+6 Hz | 4.8 @Frequency 1e+6 Hz | ASTM D150 |
| 6.0 @Frequency 60 Hz | 6.0 @Frequency 60 Hz | ASTM D150 | |
| Dielectric Strength | 11.8 kV/mm | 300 kV/in | ASTM D149 |
| Dissipation Factor | 0.040 @Frequency 1e+6 Hz | 0.040 @Frequency 1e+6 Hz | ASTM D150 |
| 0.10 @Frequency 60 Hz | 0.10 @Frequency 60 Hz | ASTM D150 | |
| Comparative Tracking Index | 125 V | 125 V | UL 746 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 351 °F | ASTM D648 |
| UL RTI, Electrical | 150 °C @Thickness 1.63 mm | 302 °F @Thickness 0.0642 in | |
| UL RTI, Mechanical with Impact | 150 °C @Thickness 1.63 mm | 302 °F @Thickness 0.0642 in | |
| UL RTI, Mechanical without Impact | 150 °C @Thickness 1.63 mm | 302 °F @Thickness 0.0642 in | |
| Flammability, UL94 | V-1 @Thickness 3.12 mm | V-1 @Thickness 0.123 in | |
| V-1 @Thickness 3.12 mm | V-1 @Thickness 0.123 in | ||