- 密度 [g/cm3]: 1.38
- 吸水率 [%]: 0.37
- 缺口冲击强度: 0.203
- 弯曲强度 [MPa]: 49.0
- 弯曲模量 [MPa]: 6.80
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.590 g/cc | 0.0213 lb/in³ | ASTM D1895 |
| Density | 1.38 g/cc | 0.0499 lb/in³ | ASTM D792 |
| Water Absorption | 0.37 % | 0.37 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0098 cm/cm | 0.0098 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 82 | 82 | ASTM D785 |
| Tensile Strength, Ultimate | 49.0 MPa | 7110 psi | ASTM D638 |
| Elongation at Break | 0.66 % | 0.66 % | ASTM D638 |
| Tensile Modulus | 8.30 GPa | 1200 ksi | ASTM D638 |
| Flexural Strength | 68.0 MPa | 9860 psi | ASTM D790 |
| Flexural Modulus | 6.80 GPa | 986 ksi | ASTM D790 |
| Compressive Strength | 191 MPa | 27700 psi | ASTM D695 |
| Poissons Ratio | 0.35 | 0.35 | ASTM D638 |
| Shear Modulus | 3.07 GPa | 445 ksi | Calculated |
| Izod Impact, Notched | 0.203 J/cm | 0.380 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.185 J/cm² | 0.880 ft-lb/in² | ASTM D256 |
| Impact | 140 | 140 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 3.20e+11 ohm-cm | 3.20e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.4 | 5.4 | ASTM D150 |
| Dielectric Strength | 8.80 kV/mm | 224 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.063 | 0.063 | ASTM D150 |
| Arc Resistance | 125 sec | 125 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 46.0 µm/m-°C @Temperature 40.0 - 130 °C | 25.6 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.380 W/m-K @Temperature 100 °C | 2.64 BTU-in/hr-ft²-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 191 °C | 376 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 306 °F | ASTM D648 |
| Flammability, UL94 | V-1 @Thickness 5.10 mm | V-1 @Thickness 0.201 in | |
| Oxygen Index | 26.5 % | 26.5 % | ASTM D2863 |
| Shrinkage | 0.46 % | 0.46 % | 72 hr, 120ºC; ASTM D1299 |