- 密度 [g/cm3]: 1.4
- 吸水率 [%]: 0.64
- 缺口冲击强度: 0.241
- 弯曲强度 [MPa]: 45.0
- 弯曲模量 [MPa]: 8.40
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.600 g/cc | 0.0217 lb/in³ | ASTM D1895 |
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D792 |
| Water Absorption | 0.64 % | 0.64 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0042 cm/cm | 0.0042 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 80 | 80 | ASTM D785 |
| Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ASTM D638 |
| Elongation at Break | 0.55 % | 0.55 % | ASTM D638 |
| Tensile Modulus | 9.20 GPa | 1330 ksi | ASTM D638 |
| Flexural Strength | 76.0 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 8.40 GPa | 1220 ksi | ASTM D790 |
| Compressive Strength | 193 MPa | 28000 psi | ASTM D695 |
| Izod Impact, Notched | 0.241 J/cm | 0.451 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.249 J/cm² | 1.19 ft-lb/in² | ASTM D256 |
| Impact | 175 | 175 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.1 | 5.1 | ASTM D150 |
| Dielectric Strength | 12.0 kV/mm | 305 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.046 | 0.046 | ASTM D150 |
| Arc Resistance | 115 sec | 115 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 75.0 µm/m-°C @Temperature 40.0 - 130 °C | 41.7 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Maximum Service Temperature, Air | 187 °C | 369 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 179 °C | 354 °F | ASTM D648 |
| Flammability, UL94 | V-1 @Thickness 5.10 mm | V-1 @Thickness 0.201 in | |
| Oxygen Index | 25 % | 25 % | ASTM D2863 |
| Shrinkage | 0.27 % | 0.27 % | 72 hr, 120ºC; ASTM D1299 |