- 密度 [g/cm3]: 1.51
- 吸水率 [%]: 0.32
- 断裂伸长率 [%]: 87.8
- 弯曲强度 [MPa]: 59.6
- 弯曲模量 [MPa]: 8.40
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.700 g/cc | 0.0253 lb/in³ | ASTM D1895 |
| Water Absorption | 0.32 % | 0.32 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0069 cm/cm | 0.0069 in/in | Post shrinkage is 0.26% at 72hr 120°C.; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 82 | 82 | ASTM D785 |
| Tensile Strength, Ultimate | 59.6 MPa | 8640 psi | ASTM D638 |
| Elongation at Break | 0.90 % | 0.90 % | ASTM D638 |
| Tensile Modulus | 10.0 GPa | 1450 ksi | ASTM D638 |
| Flexural Yield Strength | 87.8 MPa | 12700 psi | ASTM D790 |
| Flexural Modulus | 8.40 GPa | 1220 ksi | ASTM D790 |
| Compressive Yield Strength | 193.3 MPa | 28040 psi | ASTM D695 |
| Charpy Impact, Notched | 0.210 J/cm² | 0.999 ft-lb/in² | J/cm; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 3.59e+11 ohm-cm | 3.59e+11 ohm-cm | ASTM D257 |
| Dielectric Constant | 5.5 @Frequency 1e+6 Hz | 5.5 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 10.3 kV/mm | 262 kV/in | Short Term per ASTM D149. |
| Dissipation Factor | 0.058 @Frequency 1e+6 Hz | 0.058 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 140 sec | 140 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 200 °C | 392 °F | Heat Resistance; ASTM D795 |
| Deflection Temperature at 1.8 MPa (264 psi) | 178 °C | 352 °F | ASTM D648 |
| Flammability, UL94 | V-1 @Thickness 3.05 mm | V-1 @Thickness 0.120 in | |