- 拉伸强度 [MPa]: 89.6
- 弯曲模量 [MPa]: 17.2
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.70 g/cc | 1.70 g/cc | ASTM D792 | ||
| Volatiles | 6.0 - 10 % @Temperature 135 °C | 6.0 - 10 % @Temperature 275 °F | 8 min | ||
| Thickness | 711 microns | 28.0 mil | cured laminate, per ply | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Barcol | 70 | 70 | ASTM D2583 | ||
| Tensile Strength, Yield | 89.6 MPa @Temperature 23.9 °C | 13000 psi @Temperature 75.0 °F | 0° Direction, Dry; 325°F, 1000psi Cured; ASTM D638 | ||
| Tensile Modulus | 16.5 GPa @Temperature 23.9 °C | 2400 ksi @Temperature 75.0 °F | 0° Direction, Dry; 325°F, 1000psi Cured; ASTM D638 | ||
| Flexural Strength | 159 MPa @Temperature 23.9 °C | 23000 psi @Temperature 75.0 °F | Dry; 325°F, 1000psi Cured; ASTM D790 | ||
| Flexural Modulus | 17.2 GPa @Temperature 23.9 °C | 2500 ksi @Temperature 75.0 °F | Dry; 325°F, 1000psi Cured; ASTM D790 | ||
| Compressive Strength | 165 MPa @Temperature 23.9 °C | 24000 psi @Temperature 75.0 °F | Dry; 325°F, 1000psi Cured; ASTM D695 | ||
| Compressive Modulus | 16.5 GPa @Temperature 23.9 °C | 2400 ksi @Temperature 75.0 °F | Dry; 325°F, 1000psi Cured; ASTM D695 | ||
| Processing Properties | Metric | English | Comments | ||
| Gel Time | 0.800 - 1.70 min | 0.800 - 1.70 min | |||
| Shelf Life | 3.00 Month @Temperature 4.44 °C | 3.00 Month @Temperature 40.0 °F | |||
| 6.00 Month @Temperature -17.8 °C | 6.00 Month @Temperature 0.000 °F | ||||
| Descriptive Properties | |||||
| Fabric Area Weight (g/m²) | 610 | ||||
| Prepreg Resin Content (%) | 31-37 | ||||
| Resin Flow (%) | 10-30 | 325°F, 15psi | |||