- 拉伸强度 [MPa]: 29.6
- 弯曲模量 [MPa]: 14.5
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Volatiles | 2.0 - 5.0 % @Temperature 135 °C | 2.0 - 5.0 % @Temperature 275 °F | 8 min | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 29.6 MPa @Temperature 23.9 °C | 4300 psi @Temperature 75.0 °F | 0° Direction, Dry; 325°F 2500psi; ASTM D3039b | ||
| 37.2 MPa @Temperature 23.9 °C | 5400 psi @Temperature 75.0 °F | 0° Direction, Dry; 325°F 2500psi and Post-Cure; ASTM D3039b | |||
| Tensile Modulus | 15.2 GPa @Temperature 23.9 °C | 2200 ksi @Temperature 75.0 °F | 0° Direction, Dry; 325°F 2500psi and Post-Cure; ASTM D3039b | ||
| 17.2 GPa @Temperature 23.9 °C | 2500 ksi @Temperature 75.0 °F | 0° Direction, Dry; 325°F 2500psi; ASTM D3039b | |||
| Flexural Strength | 58.6 MPa @Temperature 23.9 °C | 8500 psi @Temperature 75.0 °F | Dry; 325°F 2500psi; ASTM D790 | ||
| 103 MPa @Temperature 23.9 °C | 15000 psi @Temperature 75.0 °F | Dry; 325°F 2500psi and Post-Cure; ASTM D790 | |||
| Flexural Modulus | 14.5 GPa @Temperature 23.9 °C | 2100 ksi @Temperature 75.0 °F | Dry; 325°F 2500psi and Post-Cure; ASTM D790 | ||
| Compressive Strength | 176 MPa @Temperature 23.9 °C | 25500 psi @Temperature 75.0 °F | Dry; 325°F 2500psi; ASTM D695 | ||
| 214 MPa @Temperature 23.9 °C | 31000 psi @Temperature 75.0 °F | Dry; 325°F 2500psi and Post-Cure; ASTM D695 | |||
| Thermal Properties | Metric | English | Comments | ||
| Specific Heat Capacity | 1.00 J/g-°C | 0.240 BTU/lb-°F | ASTM C351 | ||
| Thermal Conductivity | 0.389 W/m-K @Temperature 149 °C | 2.70 BTU-in/hr-ft²-°F @Temperature 300 °F | ASTM C177 | ||
| Processing Properties | Metric | English | Comments | ||
| Shelf Life | 6.00 Month @Temperature 4.44 °C | 6.00 Month @Temperature 40.0 °F | |||
| Descriptive Properties | |||||
| Filler Content (%) | 3.4-5.4 | ||||
| Nominal Prepreg Weight (oz/yd) | 30 | ||||
| Resin Flow (%) | 10-25 | 325°F, 150psi | |||
| Resin Solids Content (%) | 30-36 | ||||