- 拉伸强度 [MPa]: 89.6
- 弯曲模量 [MPa]: 15.9
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.70 g/cc | 1.70 g/cc | ASTM D792 | ||
| Volatiles | 2.0 - 5.0 % @Temperature 135 °C | 2.0 - 5.0 % @Temperature 275 °F | 8 min | ||
| Thickness | 533 microns | 21.0 mil | nominal, cured, per ply | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Barcol | 70 | 70 | ASTM D2583 | ||
| Tensile Strength, Yield | 89.6 MPa @Temperature 23.9 °C | 13000 psi @Temperature 75.0 °F | 0° Direction, Dry; 325°F Autoclave; ASTM D638 | ||
| Tensile Modulus | 17.2 GPa @Temperature 23.9 °C | 2500 ksi @Temperature 75.0 °F | 0° Direction, Dry; 325°F Autoclave; ASTM D638 | ||
| Flexural Strength | 131 MPa @Temperature 23.9 °C | 19000 psi @Temperature 75.0 °F | Dry; 325°F Autoclave; ASTM D790 | ||
| Flexural Modulus | 15.9 GPa @Temperature 23.9 °C | 2300 ksi @Temperature 75.0 °F | Dry; 325°F Autoclave; ASTM D790 | ||
| Compressive Strength | 207 MPa @Temperature 23.9 °C | 30000 psi @Temperature 75.0 °F | Dry; 325°F Autoclave; ASTM D695 | ||
| Compressive Modulus | 20.0 GPa @Temperature 23.9 °C | 2900 ksi @Temperature 75.0 °F | Dry; 325°F Autoclave; ASTM D695 | ||
| Thermal Properties | Metric | English | Comments | ||
| Specific Heat Capacity | 1.00 J/g-°C | 0.240 BTU/lb-°F | ASTM C351 | ||
| Thermal Conductivity | 0.389 W/m-K @Temperature 149 °C | 2.70 BTU-in/hr-ft²-°F @Temperature 300 °F | ASTM C177 | ||
| Processing Properties | Metric | English | Comments | ||
| Shelf Life | 6.00 Month @Temperature 4.44 °C | 6.00 Month @Temperature 40.0 °F | |||
| Descriptive Properties | |||||
| Filler Content (%) | 3.4-5.4 | ||||
| Nominal Prepreg Weight (oz/yd) | 30 | ||||
| Resin Flow (%) | 10-25 | 325°F, 150psi | |||
| Resin Solids Content (%) | 30-36 | ||||