- 拉伸强度 [MPa]: 2.14
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Volatiles | <= 3.5 % @Temperature 135 °C | <= 3.5 % @Temperature 275 °F | 8 min | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 2.14 MPa @Temperature 23.9 °C | 310 psi @Temperature 75.0 °F | Flatwise; Dry; MIL-STD 401 | ||
| 2.34 MPa @Temperature 23.9 °C | 340 psi @Temperature 75.0 °F | Flatwise; Dry; MIL-STD 401 | |||
| 290 MPa @Temperature 71.1 °C | 42000 psi @Temperature 160 °F | 0° Direction, Dry; Autoclave, 50 psi, 90min; ASTM D638 | |||
| 372 MPa @Temperature 23.9 °C | 54000 psi @Temperature 75.0 °F | 0° Direction, Dry; Oven Cure, 90min, 260°F; ASTM D638 | |||
| 414 MPa @Temperature 23.9 °C | 60000 psi @Temperature 75.0 °F | 0° Direction, Dry; Autoclave, 50 psi, 90min; ASTM D638 | |||
| Tensile Modulus | 22.1 GPa @Temperature 71.1 °C | 3200 ksi @Temperature 160 °F | 0° Direction, Dry; Autoclave, 50 psi, 90min; ASTM D638 | ||
| 23.4 GPa @Temperature 23.9 °C | 3400 ksi @Temperature 75.0 °F | 0° Direction, Dry; Oven Cure, 90min, 260°F; ASTM D638 | |||
| 24.8 GPa @Temperature 23.9 °C | 3600 ksi @Temperature 75.0 °F | 0° Direction, Dry; Autoclave, 50 psi, 90min; ASTM D638 | |||
| Compressive Strength | 207 MPa @Temperature 71.1 °C | 30000 psi @Temperature 160 °F | Dry; Autoclave, 50 psi, 90min; ASTM D695 | ||
| 331 MPa @Temperature 23.9 °C | 48000 psi @Temperature 75.0 °F | Dry; Oven Cure, 90min, 260°F; ASTM D695 | |||
| 427 MPa @Temperature 23.9 °C | 62000 psi @Temperature 75.0 °F | Dry; Autoclave, 50 psi, 90min; ASTM D695 | |||
| Compressive Modulus | 18.6 GPa @Temperature 71.1 °C | 2700 ksi @Temperature 160 °F | Dry; Autoclave, 50 psi, 90min; ASTM D695 | ||
| 24.1 GPa @Temperature 23.9 °C | 3500 ksi @Temperature 75.0 °F | Dry; Oven Cure, 90min, 260°F; ASTM D695 | |||
| 24.8 GPa @Temperature 23.9 °C | 3600 ksi @Temperature 75.0 °F | Dry; Autoclave, 50 psi, 90min; ASTM D695 | |||
| Shear Strength | 36.5 MPa @Temperature 23.9 °C | 5300 psi @Temperature 75.0 °F | Interlaminar; Dry; Autoclave, 50psi, 90min; ASTM D2344 | ||
| Optical Properties | Metric | English | Comments | ||
| Optical Density | 2.0 | 2.0 | Dm, Non-Flaming Mode; FAR 25.853, Part 25 Appendix F, Part V | ||
| 6.0 | 6.0 | Dm, Flaming Mode; FAR 25.853, Part 25 Appendix F, Part V | |||
| Processing Properties | Metric | English | Comments | ||
| Gel Time | 7.00 min | 7.00 min | |||
| Shelf Life | 6.00 Month @Temperature 4.44 °C | 6.00 Month @Temperature 40.0 °F | |||
| Descriptive Properties | |||||
| Burn Length (in) | 2.5 | Vertical Burn, 60 sec; FAR 25.853, Part 25 Appendix F, Part I (b) (4) | |||
| Climbing Drum Peel (in-lb/3in) | 10 | ASTM D1781; Dry, 75°F; Oven Cure, 90min, 260°F | |||
| 16 | ASTM D1781; Dry, 75°F; Autoclave, 50psi, 90min | ||||
| Drip | None | Vertical Burn, 60 sec; FAR 25.853, Part 25 Appendix F, Part I (b) (4) | |||
| Fabric Area Weight (g/m²) | 300 | ||||
| Heat Release, Peak (KW/m²) | 17 | FAR 25.853 Part 25 Appendix F, Part IV | |||
| Heat Release, Total (KW-min/m²) | 6 | FAR 25.853 Part 25 Appendix F, Part IV | |||
| Long Beam Flexure (in-lb/in) | 148 | Dry, 75°F; Autoclave, 50psi 90min | |||
| Prepreg Resin Content (%) | 41-47 | ||||
| Resin Flow (%) | 25 | 260°F, 150psi | |||
| Self Extinguish Time (sec) | 0 | Vertical Burn, 60 sec; FAR 25.853, Part 25 Appendix F, Part I (b) (4) | |||