- 密度 [g/cm3]: 1.85
- 断裂伸长率 [%]: 67.8
- 弯曲强度 [MPa]: 40.4
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.85 g/cc | 0.0668 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 40.4 MPa | 5860 psi | |
| Elongation at Break | 0.75 % | 0.75 % | |
| Tensile Modulus | 9.30 GPa | 1350 ksi | |
| Flexural Yield Strength | 67.8 MPa | 9830 psi | |
| Compressive Yield Strength | 157 MPa | 22800 psi | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 9.40 µm/m-°C @Temperature 20.0 °C | 5.22 µin/in-°F @Temperature 68.0 °F | in x- and y-directions |
| 15.4 µm/m-°C @Temperature 20.0 °C | 8.56 µin/in-°F @Temperature 68.0 °F | in z-direction | |
| CTE, linear, Transverse to Flow | 9.40 µm/m-°C @Temperature 20.0 °C | 5.22 µin/in-°F @Temperature 68.0 °F | |
| Specific Heat Capacity | 1.10 J/g-°C | 0.263 BTU/lb-°F | |
| Thermal Conductivity | 0.320 W/m-K | 2.22 BTU-in/hr-ft²-°F | |