- 密度 [g/cm3]: 1.4
- 吸水率 [%]: 0.28
- 缺口冲击强度: 0.315
- 弯曲强度 [MPa]: 52.0
- 弯曲模量 [MPa]: 4.80
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D792A |
| Water Absorption | 0.28 % | 0.28 % | 24 hours R.T. ASTM D570 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | Positive Mold; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D651 |
| Flexural Strength | 86.0 MPa | 12500 psi | ASTM D790 |
| Flexural Modulus | 4.80 GPa | 696 ksi | ASTM D790 |
| Compressive Strength | 207 MPa | 30000 psi | ASTM D695 |
| Izod Impact, Notched | 0.315 J/cm | 0.590 ft-lb/in | ASTM D256A |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 14.6 kV/mm | 371 kV/in | Short Time; Dry; ASTM D149 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 155 - 180 °C | 311 - 356 °F | |