- 密度 [g/cm3]: 2.0
- 吸水率 [%]: 0.1
- 缺口冲击强度: 0.683
- 弯曲强度 [MPa]: 62.0
- 弯曲模量 [MPa]: 19.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.00 g/cc | 0.0723 lb/in³ | ASTM D792A |
| Water Absorption | 0.10 % | 0.10 % | 24 hours R.T. ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 62.0 MPa | 8990 psi | ASTM D651 |
| Flexural Strength | 83.0 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 19.0 GPa | 2760 ksi | ASTM D790 |
| Compressive Strength | 193 MPa | 28000 psi | ASTM D695 |
| Izod Impact, Notched | 0.683 J/cm | 1.28 ft-lb/in | ASTM D256A |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 13.4 kV/mm | 340 kV/in | Short Time; Dry; ASTM D149 |
| Arc Resistance | 193 sec | 193 sec | ASTM D495 |
| Comparative Tracking Index | 175 - 250 V @Thickness 3.05 mm | 175 - 250 V @Thickness 0.120 in | UL PLC 3 (175-250 V) |
| Hot Wire Ignition, HWI | 60 - 120 sec @Thickness 3.05 mm | 60 - 120 sec @Thickness 0.120 in | UL PLC 1 |
| High Amp Arc Ignition, HAI | 15 - 29 arcs @Thickness 3.05 mm | 15 - 29 arcs @Thickness 0.120 in | UL PLC 3, 15-29 arcs |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 - 10.0 mm/min @Thickness 3.05 mm | 0.000 - 0.394 in/min @Thickness 0.120 in | UL PLC 0 (0-10 mm/min) |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 150 °C | 302 °F | UL RTI |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 315 °C | >= 599 °F | ASTM D648 |
| UL RTI, Electrical | 150 °C | 302 °F | |
| UL RTI, Mechanical with Impact | 150 °C | 302 °F | |
| UL RTI, Mechanical without Impact | 150 °C | 302 °F | |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 155 - 180 °C | 311 - 356 °F | |