- 密度 [g/cm3]: 1.39
- 缺口冲击强度: 0.63
- 弯曲强度 [MPa]: 53.0
- 弯曲模量 [MPa]: 7.60
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ASTM D792A |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 93 | 93 | ASTM D785 |
| Hardness, Rockwell M | 116 | 116 | ASTM D785 |
| Tensile Strength, Ultimate | 53.0 MPa | 7690 psi | ASTM D651 |
| Flexural Strength | 76.0 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 7.60 GPa | 1100 ksi | ASTM D790 |
| Compressive Strength | 193 MPa | 28000 psi | ASTM D695 |
| Izod Impact, Notched | 0.630 J/cm | 1.18 ft-lb/in | ASTM D256A |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 155 - 180 °C | 311 - 356 °F | |