- 密度 [g/cm3]: 1.41
- 吸水率 [%]: 0.3
- 缺口冲击强度: 0.683
- 弯曲强度 [MPa]: 55.0
- 弯曲模量 [MPa]: 11.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ASTM D792A |
| Water Absorption | 0.30 % | 0.30 % | 24 hours R.T. ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | Positive Mold; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 55.0 MPa | 7980 psi | ASTM D651 |
| Flexural Strength | 102 MPa | 14800 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Compressive Strength | 138 MPa | 20000 psi | ASTM D695 |
| Izod Impact, Notched | 0.683 J/cm | 1.28 ft-lb/in | ASTM D256A |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 150 - 170 °C | 302 - 338 °F | |