- 密度 [g/cm3]: 1.9
- 吸水率 [%]: 0.04
- 弯曲模量 [MPa]: 21.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.630 g/cc | 0.0228 lb/in³ | ISO 60 | ||
| Density | 1.90 g/cc | 0.0686 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.040 % | 0.040 % | ISO 62 | ||
| Linear Mold Shrinkage | 0.0015 cm/cm | 0.0015 in/in | ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 101 MPa | 14600 psi | ISO 527-1 | ||
| Elongation at Break | 0.56 % | 0.56 % | ISO 527-1 | ||
| Tensile Modulus | 22.0 GPa | 3190 ksi | ISO 527-1 | ||
| Flexural Strength | 205 MPa | 29700 psi | ISO 178 | ||
| Flexural Modulus | 21.0 GPa | 3050 ksi | ISO 178 | ||
| Compressive Strength | 293 MPa | 42500 psi | ISO 604 | ||
| Charpy Impact Unnotched | 1.17 J/cm² | 5.57 ft-lb/in² | ISO 179-1 | ||
| Charpy Impact, Notched | 0.350 J/cm² | 1.67 ft-lb/in² | ISO 179-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 8.10e+14 ohm-cm | 8.10e+14 ohm-cm | IEC 60093 | ||
| Surface Resistance | 4.30e+13 ohm | 4.30e+13 ohm | IEC 60093 | ||
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | IEC 60243-1 | ||
| Comparative Tracking Index | 200 V | 200 V | IEC 60250 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 14.0 µm/m-°C | 7.78 µin/in-°F | TMA | ||
| CTE, linear, Transverse to Flow | 31.0 µm/m-°C | 17.2 µin/in-°F | TMA | ||
| Thermal Conductivity | 0.480 W/m-K | 3.33 BTU-in/hr-ft²-°F | ASTM E1461 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 195 °C | >= 383 °F | ISO 75 Af | ||
| Deflection Temperature at 8.0 MPa | 168 °C | 334 °F | ISO 75 Cf | ||
| Flammability, UL94 | V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | |||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | ||||
| Shrinkage | 0.040 % | 0.040 % | Post Shrinkage; ISO 2577 | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| Molding Method | Compression | ||||
| Injection | |||||
| Transfer | |||||