Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Specific Gravity | 1.75 - 2.25 g/cc | 1.75 - 2.25 g/cc | ASTM D792 | ||
Mechanical Properties | Metric | English | Comments | ||
Hardness, Shore A | 58 - 72 | 58 - 72 | ASTM D2240 | ||
Tensile Strength at Break | >= 1.38 MPa | >= 200 psi | ASTM D412 | ||
Elongation at Break | 100 - 300 % | 100 - 300 % | ASTM D412 | ||
Tear Strength | 5.25 kN/m | 30.0 pli | ASTM D624 | ||
Compression Set | <= 32 % @Temperature 100 °C, Time 252000 sec | <= 32 % @Temperature 212 °F, Time 70.0 hour | ASTM D395 Method B | ||
Electrical Properties | Metric | English | Comments | ||
Volume Resistivity | 0.0080 ohm-cm | 0.0080 ohm-cm | without pressure-sensitive material; MIL-DTL-83528 | ||
0.015 ohm-cm | 0.015 ohm-cm | Post Tensile Set; MIL-DTL-83528 | |||
Shielding Effectiveness | >= 60 dB @Frequency 200000 Hz | >= 60 dB @Frequency 200000 Hz | H Field; MIL-DTL-83528 Para.4.6.12 | ||
>= 100 dB @Frequency 1.00e+10 Hz | >= 100 dB @Frequency 1.00e+10 Hz | Plane Wave; MIL-DTL-83528 Para.4.6.12 | |||
>= 105 dB @Frequency 2.00e+9 Hz | >= 105 dB @Frequency 2.00e+9 Hz | Plane Wave; MIL-DTL-83528 Para.4.6.12 | |||
>= 110 dB @Frequency 5.00e+8 Hz | >= 110 dB @Frequency 5.00e+8 Hz | E Field; MIL-DTL-83528 Para.4.6.12 | |||
>= 115 dB @Frequency 1.00e+8 Hz | >= 115 dB @Frequency 1.00e+8 Hz | E Field; MIL-DTL-83528 Para.4.6.12 | |||
Thermal Properties | Metric | English | Comments | ||
Thermal Conductivity | 2.20 W/m-K @Pressure 2.07 MPa | 15.3 BTU-in/hr-ft²-°F @Pressure 300 psi | ASTM D5470 | ||
Maximum Service Temperature, Air | 200 °C | 392 °F | |||
Minimum Service Temperature, Air | -65.0 °C | -85.0 °F | Flex TR10; ASTM D1329 | ||
Descriptive Properties | |||||
Binder | Silicone | ||||
EMP Survivability | >0.9 kA / in | ||||
Filler | Ag/Al | ||||
Grade | Military-Aerospace/B | ||||
Heat Aging | <0.01 ohm-cm | MIL-DTL-83528 Para.4.6.15 | |||
Type | B | MIL-DTL-83528 | |||
Vibration Resistance, After | <0.008 ohm-cm | MIL-DTL-83528 Para.4.6.13 | |||
Vibration Resistance, During | <0.012 ohm-cm | MIL-DTL-83528 Para.4.6.13 |