- 拉伸强度 [MPa]: 5.1
- 脆化温度 [℃]: -23.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.84 g/cc | 1.84 g/cc | at 25°C |
| Mooney Viscosity | 35 @Temperature 121 °C | 35 @Temperature 250 °F | ML 1+10 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 71 | 71 | Peak value, at 25°C |
| Tensile Strength at Break | 16.0 MPa | 2320 psi | |
| Tensile Strength, Yield | 5.10 MPa @Strain 100 % | 740 psi @Strain 100 % | |
| Elongation at Break | 210 % | 210 % | |
| Tear Strength | 20.0 kN/m | 114 pli | at 25°C |
| Compression Set | 10 % | 10 % | 70 hours at 25°C |
| 7.0 % @Temperature 100 °C | 7.0 % @Temperature 212 °F | 70 hours | |
| 10 % @Temperature 175 °C | 10 % @Temperature 347 °F | 70 hours | |
| 19 % @Temperature 200 °C | 19 % @Temperature 392 °F | 70 hours | |
| Thermal Properties | Metric | English | Comments |
| Minimum Service Temperature, Air | -20.0 °C | -4.00 °F | TR test, TR10 |
| -14.7 °C | 5.54 °F | Gehman torsion test, T10 | |
| -10.0 °C | 14.0 °F | TR test, TR70 | |
| -9.00 °C | 15.8 °F | Gehman torsion test, T2 | |
| Brittleness Temperature | -23.0 °C | -9.40 °F | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 170 °C | 338 °F | Cure Measuring Temperature |
| Cure Time | 3.00 min | 0.0500 hour | Curelastmeter |