- 拉伸强度 [MPa]: 3.7
- 脆化温度 [℃]: -14.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.92 g/cc | 1.92 g/cc | at 25°C |
| Mooney Viscosity | 31 @Temperature 121 °C | 31 @Temperature 250 °F | ML 1+10 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 77 | 77 | Peak value, at 25°C |
| Tensile Strength at Break | 14.0 MPa | 2030 psi | |
| Tensile Strength, Yield | 3.70 MPa @Strain 100 % | 537 psi @Strain 100 % | |
| Elongation at Break | 280 % | 280 % | |
| Tear Strength | 21.0 kN/m | 120 pli | at 25°C |
| Compression Set | 36 % | 36 % | 70 hours at 25°C |
| 30 % @Temperature 100 °C | 30 % @Temperature 212 °F | 70 hours | |
| 35 % @Temperature 175 °C | 35 % @Temperature 347 °F | 70 hours | |
| 60 % @Temperature 200 °C | 60 % @Temperature 392 °F | 70 hours | |
| Thermal Properties | Metric | English | Comments |
| Minimum Service Temperature, Air | -8.00 °C | 17.6 °F | TR test, TR10 |
| -4.80 °C | 23.4 °F | Gehman torsion test, T10 | |
| -2.00 °C | 28.4 °F | TR test, TR70 | |
| -1.30 °C | 29.7 °F | Gehman torsion test, T2 | |
| Brittleness Temperature | -14.0 °C | 6.80 °F | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 170 °C | 338 °F | Cure Measuring Temperature |
| Cure Time | 4.40 min | 0.0733 hour | Curelastmeter |