- 弯曲强度 [MPa]: 12.2
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Mooney Viscosity | 45.7 @Temperature 100 °C | 45.7 @Temperature 212 °F | ML(1+4), mu | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 65 | 65 | Cecilia 20 aged 168 hrs at 175°C | ||
| 73 | 73 | Press-cured 5 minutes at 190°C | |||
| 82 | 82 | Heat aged 2 weeks at 175°C | |||
| Tensile Strength, Ultimate | 12.2 MPa | 1770 psi | Cecilia 20 aged 168 hrs at 175°C | ||
| 13.0 MPa | 1890 psi | Heat aged 2 weeks at 175°C | |||
| 14.5 MPa | 2100 psi | Press-cured 5 minutes at 190°C | |||
| Elongation at Break | 182 % | 182 % | Heat aged 2 weeks at 175°C | ||
| 194 % | 194 % | Cecilia 20 aged 168 hrs at 175°C | |||
| 208 % | 208 % | Press-cured 5 minutes at 190°C | |||
| 100% Modulus | 0.00620 GPa | 0.899 ksi | Cecilia 20 aged 168 hrs at 175°C | ||
| 0.00680 GPa | 0.986 ksi | Press-cured 5 minutes at 190°C | |||
| 0.00880 GPa | 1.28 ksi | Heat aged 2 weeks at 175°C | |||
| Tear Strength | 6.30 kN/m | 35.9 pli | Trouser, Press-cured 5 minutes at 190°C; DIN 53507 | ||
| 23.0 kN/m | 131 pli | Press-cured 5 minutes at 190°C; ISO 34 | |||
| Compression Set | 25 % | 25 % | 70 hrs at 150°C | ||
| 77 % | 77 % | 22 hrs at 150°C; VW PV 3307 | |||
| Thermal Properties | Metric | English | Comments | ||
| Glass Transition Temp, Tg | -31.7 °C | -25.1 °F | By DSC | ||
| Descriptive Properties | |||||
| Armeen® 18D | 0.5 phr | ||||
| Bisoflex T810T | 5 phr | ||||
| Change in Volume | 13 % | Cecilia 20 aged 168 hrs at 175°C | |||
| Change in Weight | 9 % | Cecilia 20 aged 168 hrs at 175°C | |||
| HVA® #2 coagent | 2 phr | ||||
| Mooney Scorch at 121°C, t5 | 10.9 metric minutes | Time for 5 unit rise | |||
| Naugard® 445 antioxidant | 1 phr | ||||
| Perkadox 14/40 | 5 phr | ||||
| Stearic Acid | 1.5 phr | ||||
| Sterling SO-N550 black | 65 phr | ||||
| Vamac® DP | 100 phr | ||||