- 弯曲强度 [MPa]: 11.7
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Mooney Viscosity | 41.7 @Temperature 100 °C | 41.7 @Temperature 212 °F | ML(1+4), mu | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 58 | 58 | Cecilia 20 aged 168 hrs at 175°C | ||
| 72 | 72 | Press-cured 5 minutes at 190°C | |||
| 82 | 82 | Heat aged 2 weeks at 175°C | |||
| Tensile Strength, Ultimate | 11.7 MPa | 1700 psi | Cecilia 20 aged 168 hrs at 175°C | ||
| 12.5 MPa | 1810 psi | Heat aged 2 weeks at 175°C | |||
| 14.9 MPa | 2160 psi | Press-cured 5 minutes at 190°C | |||
| Elongation at Break | 187 % | 187 % | Heat aged 2 weeks at 175°C | ||
| 195 % | 195 % | Press-cured 5 minutes at 190°C | |||
| 252 % | 252 % | Cecilia 20 aged 168 hrs at 175°C | |||
| 100% Modulus | 0.00400 GPa | 0.580 ksi | Cecilia 20 aged 168 hrs at 175°C | ||
| 0.00740 GPa | 1.07 ksi | Press-cured 5 minutes at 190°C | |||
| 0.00770 GPa | 1.12 ksi | Heat aged 2 weeks at 175°C | |||
| Tear Strength | 7.00 kN/m | 39.9 pli | Trouser, Press-cured 5 minutes at 190°C; DIN 53508 | ||
| 19.8 kN/m | 113 pli | Press-cured 5 minutes at 190°C; ISO 34 | |||
| Compression Set | 36 % | 36 % | 70 hrs at 150°C | ||
| 73 % | 73 % | 22 hrs at 150°C; VW PV 3307 | |||
| Thermal Properties | Metric | English | Comments | ||
| Glass Transition Temp, Tg | -31.2 °C | -24.2 °F | By DSC | ||
| Descriptive Properties | |||||
| Activator OC(TAC) | 2 phr | ||||
| Armeen® 18D | 0.5 phr | ||||
| Bisoflex T810T | 5 phr | ||||
| Change in Volume | 14 % | Cecilia 20 aged 168 hrs at 175°C | |||
| Change in Weight | 9 % | Cecilia 20 aged 168 hrs at 175°C | |||
| Mooney Scorch at 121°C, t5 | 31.9 metric minutes | Time for 5 unit rise | |||
| Naugard® 445 antioxidant | 1 phr | ||||
| Perkadox 14/41 | 5 phr | ||||
| Stearic Acid | 1.5 phr | ||||
| Sterling SO-N550 black | 65 phr | ||||
| Vamac® DP | 100 phr | ||||