- 弯曲强度 [MPa]: 15.4
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 68 | 68 | |||
| 72 | 72 | Air aged 7 days at 150°C | |||
| 86 | 86 | Air aged 14 days at 175°C | |||
| Tensile Strength, Ultimate | 15.4 MPa | 2230 psi | Air aged 14 days at 175°C | ||
| 15.6 MPa | 2260 psi | Air aged 7 days at 150°C | |||
| 16.1 MPa | 2340 psi | ||||
| Elongation at Break | 193 % | 193 % | Air aged 14 days at 175°C | ||
| 272 % | 272 % | ||||
| 278 % | 278 % | Air aged 7 days at 150°C | |||
| 100% Modulus | 0.00640 GPa | 0.928 ksi | |||
| 0.00680 GPa | 0.986 ksi | Air aged 7 days at 150°C | |||
| 0.00950 GPa | 1.38 ksi | Air aged 14 days at 175°C | |||
| Tear Strength | 34.0 kN/m | 194 pli | Die C, at 23°C | ||
| Compression Set | 20 % | 20 % | 70 hrs at 150°C, method B, plied | ||
| 28 % | 28 % | 168 hrs at 150°C, method B, plied | |||
| Thermal Properties | Metric | English | Comments | ||
| Glass Transition Temp, Tg | -23.0 °C | -9.40 °F | By DSC | ||
| Descriptive Properties | |||||
| Armeen® 18D | 0.5 parts | ||||
| Diak No. 1 | 1.5 parts | ||||
| DOTG Coaccelerator | 4 parts | ||||
| FEF Black(N550) | 60 parts | ||||
| Naugard® 445 antioxidant | 2 parts | ||||
| Stearic Acid | 1.5 parts | ||||
| TP-760 | 10 parts | ||||
| Vamac® GLS | 100 parts | ||||
| Vanfre® VAM | 1 part | ||||