- 密度 [g/cm3]: 1.22
- 弯曲强度 [MPa]: 9.3
- 脆化温度 [℃]: -43.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | |
| Mooney Viscosity | 64 @Temperature 100 °C | 64 @Temperature 212 °F | ML 1 + 4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 65 | 65 | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tensile Strength, Ultimate | 9.30 MPa | 1350 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Elongation at Break | 425 % | 425 % | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 100% Modulus | 0.00330 GPa | 0.479 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 300% Modulus | 0.00790 GPa | 1.15 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tear Strength | 37.1 kN/m | 212 pli | Die C, Vulcanizate, Press cured, TC95 +3min at 160°C |
| Compression Set | 75 % @Temperature 100 °C | 75 % @Temperature 212 °F | Pellets cured MDR TC95 + 15 min at 160°C, 22 hr at 100°C; Method B |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -43.0 °C | -45.4 °F | Temperature Retraction, TR-10 |