- 密度 [g/cm3]: 1.283
- 弯曲强度 [MPa]: 15.13
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.283 g/cc | 0.04635 lb/in³ | |
| Mooney Viscosity | 44 @Temperature 100 °C | 44 @Temperature 212 °F | ML 1 + 4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 90 | 90 | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Hardness, Shore D | 46 | 46 | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tensile Strength, Ultimate | 15.13 MPa | 2194 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Elongation at Break | 213 % | 213 % | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 50% Modulus | 0.00570 GPa | 0.827 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 100% Modulus | 0.00843 GPa | 1.22 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 200% Modulus | 0.01448 GPa | 2.100 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Compression Set | 53 % @Temperature 100 °C | 53 % @Temperature 212 °F | Pellets cured MDR TC95 + 15 min at 160°C, 22 hr at 100°C; Method B |