- 弯曲强度 [MPa]: 40.3
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.80 - 1.90 g/cc | 1.80 - 1.90 g/cc | ASTM D792-66 | ||
| Brookfield Viscosity | 2950 cP @Temperature 23.9 °C | 2950 cP @Temperature 75.0 °F | #3 spindle @ 20 rpm; ASTM D2393 | ||
| Linear Mold Shrinkage | 0.00020 cm/cm | 0.00020 in/in | ASTM D2566-69 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 85 @Temperature 23.9 °C | 85 @Temperature 75.0 °F | ASTM D2240 | ||
| Tensile Strength, Ultimate | 40.3 MPa | 5850 psi | |||
| Compressive Strength | 60.7 MPa | 8800 psi | ASTM D695 | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 210 - 240 min @Temperature 24.0 °C | 3.50 - 4.00 hour @Temperature 75.2 °F | demold time | ||
| Pot Life | 14 - 17 min @Temperature 24.0 °C | 14 - 17 min @Temperature 75.2 °F | 1 lb. mass | ||
| Descriptive Properties | |||||
| Mix Ratio | 1:1 by weight or volume | ||||